N.CW104C Cobalt Beryllium Copper Rod / Bars Available State A(TB00),H(TD04),AT(TF00),HT(TH04)
Product Description:
Name: Cobalt Beryllium Copper Rod / Bars
Grade: N.CW104C
End Product Form: Rods/ Bars
Standard: ASTM B441
State of product: A(TB00),H(TD04),AT(TF00),HT(TH04)
Processing: Seamless / Welding
Feature: Anti corrosion and wear resistant materials
Package: Pack in coil+waterproofing winding film+Drier+Wooden Case
Specification: 1, Length: according customers' requirement
2, Diameter: 8-30mm
CUBERYLLIUM ®-750 also named -C17500 (CDA 750) combine moderate yield strength, up to 960Mpa(140ksi), with electrical and thermal conductivity from 45 to 60 % of pure copper. Alloys 750 and 751 are available in wrought product forms and can be supplied fully hardened. Hardened products are identified by the temper designation AT or HT, and have good formability.
Chemical Composition of N.CW104C Cobalt Beryllium Copper Alloys:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt | Nickel | Cobalt+Nickel | Lead | Copper |
| Cuberyllium-C750 | C17500 | 0.40-0.70 | 2.4～2.7 | - | - | - | Balance |
Related material specifications of N.CW104C Cobalt Beryllium Copper Alloys:
Rods/Bars/Tubes: ASTM B441, SAE J461, 463; RWMA Class 3
Strips: ASTM B534
Sheets: ASTM B534
Wires: ASTM B441
Plates: ASTM B534, SAE J461, RWMA Class 3
European Standards: CuCo2Be, CuCoBe, UNS. C17500, Alloy 10, DIN 2.1285, CW104C to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by ASTM.
Typical Physical Properties of N.CW104C Cobalt Beryllium Copper Alloys:
| Density | 8.83 | g/cm3 |
| Density before age hardening | 8.75 | g/cm3 |
| Melting Range | 1000~1070 | ℃ |
| Elastic Modulus | 14.1 | (kg/mm2 (103) |
| Thermal Expansion Coefficient | 18 x 10 -6 | 20 °C to 200 °C m/m/°C |
| Thermal Conductivity | 0.48 | cal/(cm-s-°C) |
Typical Applications for N.CW104C Cobalt Beryllium Copper Alloys:
| Product Category | Product | Reason Category | Reason |
| Industrial | Tooling for Plastic Molds | Conductivity (Electrical) | Electrical Conductivity |
| Tooling for Plastic Molds | Conductivity (Thermal) | Thermal Conductivity |
| Tooling for Plastic Molds | Corrosion Resistance | Corrosion Resistance |
| Tooling for Plastic Molds | Mechanical Properties | High Strength |
| Tooling for Plastic Molds | Softening Resistance | Resistance to Thermal Softening |
Mechanical and Electrical Properties of N.CW104C Cobalt Beryllium Copper Rod / Bars:
| Temper(*) | Diameter | Heat Treatment | Tensile Strength Mpa | Elongation Percent (Min) | Electrical Conductivity Percent IACS | Hardness Rockwell B Scale |
| A(TB00) | ALL SIZE | / | 240~380 | 20~40 | 20~35 | B20~50 |
| H(TD04) | ALL SIZE | / | 440~550 | 10~20 | 20~35 | B20~30 |
| AT(TF00) | ALL SIZE | 3 hr 480℃ | 680~900 | 10~30 | 45~60 | B92~100 |
| HT(TH04 | ALL SIZE | 2 hr 480 ℃ | 750~960 | 5~30 | 48~60 | B95~102 |
Product Photo:
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.
Product Tags:
|
|
N CW104C Cobalt Beryllium Copper Rod Bars State A TB00 H TD04 AT TF00 HT TH04 Images
|